Surface functionalisation of self-assembled quantum dot microlasers with a DNA aptamer

Surface functionalisation of self-assembled colloidal quantum dot supraparticle lasers with a Thrombin Binding Aptamer (TBA-15) has been demonstrated. Self-assembly of CdSSe/ZnS alloyed core/shell microsphere-shape CQD supraparticles emitting at 630 nm was carried out using an oil-in-water emulsion technique, yielding microspheres with an oleic acid surface and an average diameter of 7.3 ± 5.3 μm. Surface modification of the microspheres was achieved through a ligand exchange with mercaptopropionic acid and subsequent attachment of TBA-15 using EDC/NHS coupling, confirmed by zeta potential and Fourier Transform IR spectroscopy. Lasing functionality between 627 nm and 635 nm was retained post-functionalisation with oleic acid- and TBA-coated microspheres exhibiting laser oscillation with thresholds as low as 4.10 ± 0.37 mJ.cm-2 and 7.23 ± 0.78 mJ.cm-2 respectively

Self-assembled cadmium-free semiconductor microspheres based on colloidal quantum dots

A method for the fabrication of cadmium-free, photoluminescent (PL) quantum dot supracrystal microspheres (MS) is implemented, creating red emitting MS. The overall aim is to characterise and develop MS acting as optical microresonators, and to explore their applications in miniature lasers for bioimaging and biosensing using non-toxic semiconductor materials. Fabrication of whispering gallery mode (WGM) microlasers via self-assembly of colloidal quantum dots (CQDs) has been previously achieved with the caveat of employing toxic metals, and resulting in MS with low solubility [1,2]. Non-toxic InP/ZnS CQDs represent a heavy-metal free alternative for luminescent applications and have been demonstrated as a laser material [3]. By utilising the self-assembly of oleate capped CQDs via an oil-in-water emulsion technique, MS were formed and suspended in water with polyvinyl alcohol as a surfactant. The following step included the addition of polyvinylpyrrolildone, then ammonia and tetraethyl orthosilicate for a thin (<5 nm) coating of silica to allow for improved solubility in water. The MS characterisation consisted of: (i) optical microscope imaging to ascertain the size and size distribution of 5-45 µm; (ii) UV-visible absorption spectroscopy and Scanning Electron Microscopy; (iii) optical pumping with a 355 nm, 5 ns pulsed Nd:YAG laser at a 10 Hz repetition rate with a beam spot area of 2.6 ± 1.5 x10-5 cm2 for PL spectra measurements. Optical pumping demonstrated the resulting MS PL ability, which differs significantly from their QD precursor’s comparatively Gaussian PL. Details of the results of the MS synthesis and of the optical characterisation at different wavelengths will be discussed